High Wax Casting Resin (300H)
Download InstructionsA jewelry casting resin with a high wax content of 80%, which is popular in the Middle East jewelry market
- High wax content 80%
- Low shrinkage, dimensionally stable
- Smooth surface, clear sharp corners
- Casting with low thermal expansion
- Simple post-processing
- Suitable for casting gold, silver
High Wax Resin Print Samples
Specifications of High Wax Casting Resin (300H)
Content Data value Testing method color Green Viscosity 290~310 cps(25℃) ASTM D1084-1997 Density 1.1~1.2g/cm³ ASM D1875-69(1980) Shrinkage ≤0.3% Capillary method Hardness 30A~40D ASTM D2240 05(2010) choose high-strength gypsum powder can achieve better casting effect
Recommend:
1.Prestige OPTIMA : https://www.certus-int.com/optima
2.Gilcast HS SOFT : https://www.srldental.com
3.GRS : https://www.goodwin.co.uk/4.TT resin powder（TECAST RESINCAST）
Precautions for use:
White wax is easy to solidify at low temperature.If the ambient temperature is low, first heat the resin to above 25 degrees and stir evenly. The temperature of the printing chamber is above 25 degrees Celsius during printing.
you may also need these machines
Gold Giant 14k
High precision, large size jewelry HD industrial printer
Build Size 208*128*210mm
Printing Speed 10~15mm/h
Accuracy ±16.8μm
Resolution 13320*5120
Packing Weight 37.5kg
Packing size 580*580*1030mm
Gold Mini 9k
Small size fast 3D printer for jewelry，Small body, big power
Build Size 143*89*150mm
Printing Speed 15~20mm/h
Accuracy ±18μm
Resolution 8520*4320
Packing Weight 21kg
Packing size 400*400*580mm
HP-J800
High power,large volume,suitable for production factories
Curing Size 310*358*170mm
Curing Power 800w
Curing Time 120min(max)
UV Lamp Life 1000h
Packing Weight 19kg
Packing size 500*437*505mm
Enable 3D Digital Production